Analisis Variasi Arus Pengelasan Mig pada Baja ST.42 terhadap Kekuatan Tarik Sambungan dan Metallographic Analysis

Wisma Soedarmadji; Tulus Subagyo; Mohammad Effendi; Ahmad Nur Faizin

doi:10.35891/qdt4k971

Authors

Wisma Soedarmadji Universitas Yudharta Pasuruan
Tulus Subagyo Universitas Yudharta Pasuruan
Mohammad Effendi Universitas Yudharta Pasuruan
Ahmad Nur Faizin Universitas Yudharta Pasuruan, Indonesi

DOI:

https://doi.org/10.35891/qdt4k971

Keywords:

Current Strength, Metallographic Analysis Test, MIG Welding, Tensile Test

Abstract

In welding techniques to produce good welded joints, one of the factors that must be considered is the welding current. In this study, the welding current used was 125A and 130A with single V-shaped seams and double tapered seams using a feed feed of 1.0 mm diameter and type of material. used is ST.42 steel plate. The results of research that has been carried out regarding variations in current strength on the tensile strength of joints and metallographic analysis can be concluded that the single V seam using the Metal inert gas (MIG) welding process has decreased tensile strength in specimen 2 at a stress of 35.46 kg/mm2, strain received was 17.28%, and the grain size had an average diameter of 0.0635 mm or 63.5 μm. The double tapered seam shape using the Metal inert gas (MIG) welding process saw a decrease in tensile strength in specimen 2 at a stress of 13.8 kg/mm2, the accepted strain was 4.38%, and the grain size had an average diameter of 0, 0635 mm or 63.5 μm.

References

Gumara, R. A., & Drastiawati, N. S. (2021). Pengaruh Variasi Arus Listrik Pengelasan Metal Inert Gas (MIG) Terhadap Kekuatan Tarik Sambungan Las Pada Baja Karbon ASTM A36. Jurnal Teknik Mesin Unesa, 9(3), 65–68.

Huda, M. H., Jokosisworo, S., & Yudo, H. (2017). Analisa Pengaruh Pengelasan TIG Dan MIG Terhadap Kekuatan Tarik Dan Bending Pada Sambungan Pelat Alumunium 5083. Kapal: Jurnal Ilmu Pengetahuan Dan Teknologi Kelautan, 14(1), 14–20. https://doi.org/10.14710/kpl.v14i1.14569

Ihza, P., & Ramadhani, C. (2023). Oleh Pradipta Ihza Cahya Ramadhani 1910502045.

Ishak, S., Asiri, M. H., & Kamil, K. (2020). Analisis Sambungan Las MIG pada Baja Karbon Rendah Variasi Kampuh Las V, I dan K terhadap Kekuatan Tarik Sahional Ishak (1) , Muhammad Halim Asiri (2) dan Kusno Kamil (3) (1) Mahasiswa Program Magister Teknik Mesin, Universitas Muslim Indonesia (2)(3) Dos. 5–11.

Jasman, & Huda, N. (2019). Pengaruh Kuat Arus terhadap Uji Tarik Baja Karbon Rendah Menggunakan Metal Inert Gas (MIG). Ranah Research, 2(1), 219–229.

Karmanianto, R. B., Carsoni, C., & Ma’mun, H. (2021). Pengaruh Variasi Sudut Kampuh Dan Kuat Arus Terhadap Kekuatan Dan Kekerasan St 60 Pada Pengelasan Smaw. Device, 11(1), 52–57. https://doi.org/10.32699/device.v11i1.1805

Marthiana, W., Mahyoedin, Y., Duskiardi, D., & Rahim, A. (2020). Analisa Pengaruh Variasi Arus Listrik Pengelasan Terhadap Kekuatan Sambungan Pengelasan MIG Pada Material ST 37. Jurnal Kajian Teknik Mesin, 5(2), 140–144. https://doi.org/10.52447/jktm.v5i2.4217

Prasetya, I. E., Kosjoko, K., & Mufarida, N. A. (2022). Pengaruh Variasi Arus Listrik Dan Kampuh Las Terhadap Kekuatan Tarik Dan Struktur Mikro Sambungan Las Tig Pada Aluminum Alloy 6061. Elemen : Jurnal Teknik Mesin, 9(1), 14–23. https://doi.org/10.34128/je.v9i1.187

Priyono, B., Irzal, I., Nurdin, H., & Primawati, P. (2021). Analisis Pengaruh Variasi Kuat Arus Pengelasan Metal Inert Gas (Mig) Terhadap Ketangguhan Material Sambungan Las Pada Baja St 37. Jurnal Vokasi Mekanika (VoMek), 3(3), 8–14. https://doi.org/10.24036/vomek.v3i3.207

Soedarmadji, W., & Abdillah, M. I. (2021). Metallographic Analysis Of Coil Springs Against Temperature Variations Using ASTM E-122 and ASTM E-562. Journal Knowledge Industrial Engineering, 8(3), 207–214.

Syaifudin, M. (2023). Analisa Pengaruh Kuat Arus Plat Baja ST 42 Pada Pengelasan GMAW Terhadap Uji Kekerasan Dan Mikrostruktur. 6(2), 78–87.

Towijaya, T., Pujiono, A., & Baihaki, I. (2024). Pengaruh Variasi Arus pada Las Mig terhadap Sifat Mekanik Sambungan Las pada Baja ST-60. Jurnal Ilmiah Surya Teknika, 8(1), 6–10.

Wisma, S. (2020). Pengaruh Pengelasan Shielded Metal Arc Welding (SMAW) pada Mild Steel S45C di Daerah HAZ dengan Pengujian Metalografi. Mechanical and Manufacture Technology, 1(1), 12–17.

Wisma Soedarmadji, Hendrik Saputra, & Tulus Subagyo. (2017). Pengaruh Pengelasan Shielded Metal Arc Welding (Smaw) Pada KampuhiTertutup Dan Kampuh I Terbuka Terhadap Kekuatan Tarik Dan Mikro Struktur.